Stick Fast

5 and 20 minute Clear Epoxy – Tech Data Sheet

Description:

Stick Fast 5 and 20 Minute Epoxies are a two part 1:1 mix ratio, free flowing in viscosity unfilled adhesive that mixes easily at room temperature and contains no solvents.  Both are formulated for structural bonding and coating applications.  Curing to a tough semi-rigid material; they are suitable for wood, ceramics, glass, metal, polyester, rubber, and most plastics.  They have excellent resistance to water, salt spray, inorganic acids and bases, and most organic solvents.

Typical Properties:

Color                                                Clear

Viscosity                                          Part A: 12,000 cps

                                                         Part B: 13,000 cps

                                                         Mixed: 12,500 cps

Pot Life (20gm mass)                       5 minute epoxy:           3 to 5 minutes

                                                         20 minute epoxy:         20-30 minutes

Handling Cure (20gm mass):            5 minute epoxy:           20 to 30 minutes

                                                         20 minute epoxy:         60-120 minutes

Hardness (Method: Shore D):          80

Instructions:

·       Bring both components to room temperature prior to mixing.  Mix thoroughly one part A to one part B by volume or weight.

·       Allow to cure undisturbed until product is fully gelled or tack-free to the touch.

·       Clean up with a suitable organic solvent such as MEK, Acetone, or chlorinated solvent.

Tech Data:

Specific gravity:                   Part A:                   1.16

                                             Part B:                   1.15

                                             Mixed:                   1.16

Tensile strength Lap Shear (Al to Al):               2300psi

Tensile elongation:                                             3-5%

Tensile Strength:                                                7000psi

Temperature range:                                            -40^oC to 130^oC

Linear Coefficient of thermal expansion:           (x10(6))/C/62

Dielectric constant (25^oC, 100Hz):                    4.5

Dielectric Strength:                                            410v/mil

Volume Resistivity:                                            8x10¹⁴ ohm-cm